Grade 410 / 1.4006 is a hardenable martensitic stainless steel. Alloy designations of 1.4006 are similar, but may not be considered as a direct equivalent to: 410S, UNS S41000, and 410S21.
Image Credit: Shutterstock/dedek
This grade of steel is supplied in the form of bar. It exhibits moderate corrosion resistance in non-chloride containing environments.
Chemical Composition
| 1.4006 Steel |
EN 10088-3:2005 |
| Chemical Element |
% Present |
| Carbon (C) |
0.08 - 0.15 |
| Chromium (Cr) |
11.50 - 13.50 |
| Silicon (Si) |
0.0 - 1.00 |
| Manganese (Mn) |
0.0 - 1.50 |
| Phosphorous (P) |
0.0 - 0.04 |
| Sulphur (S) |
0.0 - 0.02 |
| Nickel (Ni) |
0.0 - 0.75 |
| Iron (Fe) |
Balance |
Properties
| Physical Property |
Value |
| Density |
7.75 g/cm³ |
| Thermal Expansion |
9.9 x 10-6/K |
| Modulus of Elasticity |
300 GPa |
| Thermal Conductivity |
24.9 W/m.K |
| Electrical Resistivity |
0.57 x 10-6 Ω.m |
| Bar - Up to 160mm Dia or Thickness |
EN 10088-3:2005 |
| Mechanical Property |
Value |
| Proof Stress |
450 Min MPa |
| Tensile Strength |
650 - 850 MPa |
| Elongation A |
15 Min % |
This information has been sourced, reviewed and adapted from materials provided by Aalco - Ferrous and Non-Ferrous Metals Stockist.