UNS C19000 Copper Wires - Mechanical Properties

UNS C19000 copper alloy has a copper content of not less than 98.6%.

The following table outlines the mechanical properties of UNS C19000 wires as a function of heat treatment and thickness.

Temper Thickness Tensile Str. Yield Str. Elong Shear Str.
HR01 2 mm (0.08 in) 552 MPa (80 ksi) 483 MPa (70 ksi) 13% 276 MPa (40 ksi)
HR02 2 mm (0.08 in) 607 MPa (88 ksi) 503 MPa (73 ksi) 8% 296 MPa (43 ksi)
HR04 2 mm (0.08 in) 669 MPa (97 ksi) 531 MPa (37 ksi) 5% 338 MPa (49 ksi)
HR08 2 mm (0.08 in) 758 MPa (110 ksi) 552 MPa (81 ksi) 4% 393 MPa (57 ksi)
HR10 2 mm (0.08 in) 793 MPa (115 ksi) 558 MPa (81 ksi) 3% 414 MPa (60 ksi)
TF00 2 mm (0.08 in) 448 MPa (65 ksi) 276 MPa (40 ksi) 25% 241 MPa (35 ksi)

The chemical composition of UNS C19000 copper alloy is outlined in the following table.

Element Content (%)
Copper, Cu 98.6
Nickel, Ni 0.9-1.3
Zinc, Zn 0.8
Phosphorous, P 0.15-0.35
Iron, Fe 0.1
Lead, Pb 0.05



 