Polyamide 6/6 - Nylon 6/6 - PA 6/6 40% Glass Bead Filled

Polymer Type

Thermoplastic

Advantages

Increased rigidity without the distortion problems associated with glass fibre reinforcement. High compressive strength compared with unmodified grades of Nylon 6/6.

Disadvantages

Reduced notched impact strength compared with unmodified polyamide 6/6. No improvement in HDT.

Typical Properties

Property

Value

Density (g/cm3)

1.45

Surface Hardness

RM98

Tensile Strength (MPa)

60

Flexural Modulus (GPa)

4

Notched Izod (kJ/m)

0.05

Linear Expansion  (/°C x 10-5)

3.5

Elongation at Break (%)

2.5

Strain at Yield (%)

N/A

Max. Operating Temp. (°C)

80

Water Absorption (%)

0.6

Oxygen Index (%)

22

Flammability UL94

HB

Volume Resistivity (log ohm.cm)

14

Dielectric Strength (MV/m)

15

Dissipation Factor 1kHz

0.2

Dielectric Constant  1kHz

8

HDT @ 0.45 MPa (°C)

220

HDT @ 1.80 MPa (°C)

157

Material. Drying  hrs @ (°C)

3 @ 95

Melting Temp. Range (°C)

280 - 300

Mould Shrinkage (%)

1

Mould Temp. Range (°C)

40 -  60

Applications

Automotive wheel trims, domestic cooker components, fuse box housings, precision engineering components.

 

Source : Abstracted from Plascams

For more information on Plascams please visit RAPRA Technology Ltd.

 

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.