Copper Rods (UNS C16500) - Mechanical Properties

Jan 31 2013

UNS C16500 has a copper content of not less than 98.6%.

Tabulated below are the mechanical properties of UNS C16500 rods as a function of heat treatment and thickness.

Temper Thickness Tensile Str. Yield Str. Elong. Rockwell Fatigue Str.
B C F 30T
OS050 12.7mm (0.5in) 276MPa (40ksi) 97MPa (14ksi) 53% - - 62 - 138MPa (20ksi)

The chemical composition of UNS C16500 copper alloy is outlined in the following table.

Elements Content (%)
Cadmium, Cd 0.6-1.0
Tin, Sn 0.50-.7
Iron, Fe 0.02
Copper, Cu Remainder

Equivalent materials to UNS C16500 copper alloy are:

  • ASTM B105
  • ASTM B9

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
(Logout)
Your comment type
Submit

Editorial Highlights

Sponsored Content

Newsletters you may be interested in

See all Newsletters »

Terms

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.

Provide Feedback