Dec 13 2012
UNS C61300 has a copper content of not less than 90.3%.
Tabulated below are the mechanical properties of UNS C61300 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
Fatigue Str. |
B |
C |
F |
30T |
O60 |
3.18mm (0.125in) |
552MPa (80ksi) |
276MPa (40ksi) |
40% |
82 |
- |
- |
- |
359MPa (52ksi) |
193MPa (28ksi) |
|
12.7MPa (0.5in) |
538MPa (78ksi) |
241MPa (35ksi) |
42% |
81 |
- |
- |
- |
345MPa (50ksi) |
179MPa (26ksi) |
|
25.4MPa (1in) |
524MPa (76ksi) |
228MPa (33ksi) |
42% |
79 |
- |
- |
- |
310MPa (45ksi) |
172MPa (25ksi) |
|
76mm (3in) |
483MPa (70ksi) |
207MPa (30ksi) |
40% |
78 |
- |
- |
- |
290MPa (42ksi) |
145MPa (21ksi) |
The chemical composition of UNS C61300 copper alloy is outlined in the following table.
Elements |
Content (%) |
Al |
6.0-7.5 |
Fe |
2.0-3.0 |
Sn |
0.20-0.50 |
Mn |
0.2 |
Ni |
0.15 |
Si |
0.1 |
Zn |
0.1 |
P |
0.015 |
Pb |
0.01 |
Cu |
Remainder |
Equivalent materials to UNS C61300 copper alloy are given in the table below.
ASTM B111 |
ASTM B150 |
ASTM B169 |
ASTM B171 |
QQ C450 |
ASTM B315 |
ASTM B432 |
ASTM B608 |
ASTM F467 |
ASTM F468 |