Dec 13 2012
Aluminum bronze UNS C63200 has a copper content of not less than 82%.
The following table shows the mechanical properties of UNS C63200 plates as a function of heat treatment and thickness.
| Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
| B |
C |
F |
30T |
| O50 |
6.35 mm. (0.25in.) |
689MPa (100ksi) |
345MPa (50ksi) |
20% |
92 |
- |
- |
- |
|
12.7 mm. (0.5 in.) |
655MPa (955ksi) |
324MPa (47ksi) |
22% |
89 |
- |
- |
- |
|
25.4 mm. (1 in.) |
621MPa (90ksi) |
310MPa (45ksi) |
25% |
85 |
- |
- |
- |
Equivalent materials to UNS C63200 copper alloy are provided in the table below.
- ASTM B124
- ASTM B150
- ASTM B283
The chemical composition of UNS C63200 copper alloy is outlined in the following table.
| Element |
Content (%) |
| Aluminum, Al |
8.7-9.5 |
| Nickel, Ni |
4.0-4.8 |
| Iron, Fe |
3.5-4.3 |
| Manganese, Mn |
1.2-2.0 |
| Silicon, Si |
0.1 |
| Lead, Pb |
0.02 |
| Copper, Cu |
Remainder |