Nov 30 2012
UNS C35330 DZR brass has a copper content of not less than 59.5%.
The following table shows the mechanical properties of UNS C35330 rod and wire as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
H02 |
12 mm (≤1/2 in) |
- |
- |
|
65 |
- |
- |
54 |
|
12 mm (≤1/2 in) |
- |
- |
- |
85 |
- |
- |
- |
|
12 mm (≤1/2 in) |
385 MPa (55 ksi) |
290 MPa (40 ksi) |
10% |
- |
- |
- |
- |
|
12 – 25 mm (1/2 – 1 in) |
- |
- |
- |
75 |
- |
- |
- |
|
12 – 25 mm (1/2 – 1 in) |
- |
- |
- |
40 |
- |
- |
- |
|
12 – 25 mm (1/2 – 1 in) |
350 MPa (50 ksi) |
215 MPa (35 ksi) |
20% |
|
- |
- |
|
25 – 50 mm (1 – 2 in) |
- |
- |
- |
65 |
- |
- |
- |
|
25 – 50 mm (1 – 2 in) |
- |
- |
- |
40 |
- |
- |
- |
|
25 – 50 mm (1 – 2 in) |
330 Ma (45 ksi) |
120 MPa (30 ksi) |
30% |
- |
- |
- |
- |
|
>50 mm (>2 in) |
335 MPa (40 ksi) |
180 MPa (25 ksi) |
35% |
- |
- |
- |
- |
|
>50 mm (>2 in) |
- |
- |
- |
30 |
- |
- |
- |
|
>50 mm (>2 in) |
- |
- |
- |
55 |
- |
- |
- |
O60 |
25 mm (≤1 in ) |
- |
- |
- |
40 |
- |
- |
- |
|
25 mm (≤1 in ) |
345 MPa (40 ksi) |
140 MPa (25 ksi) |
25% |
- |
- |
- |
- |
|
25 mm (≤1 in ) |
- |
- |
- |
70 |
- |
- |
- |
The chemical composition of UNS C35330 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
59.5-64 |
Lead, Pb |
1.3-3.5 |
Arsenic, As |
0.02-0.25 |
Zinc, Zn |
Remainder |