Low Silicon Brass Forgings (UNS C68350) - Mechanical Properties

Jan 8 2013

Low silicon brass UNS C68350 has a copper content of not less than 90%.

The following table shows the mechanical properties of UNS C68350 forgings as a function of heat treatment.

Temper Tensile Str. Elong. Rockwell Shear Str.
B C F 30T
M10 400MPa (58ksi) - - - - - -
430MPa (62ksi) 45% 63 - - - 226MPa (32ksi)
460MPa (66ksi) - - - - - -

The chemical composition of UNS C68350 copper alloy is outlined in the following table.

Element Content (%)
Copper, Cu 59-64
Tin, Sn 0.6
Silicon, Si 0.3-1
Aluminum, Al 0.3
Nickel, Ni 0.2
Iron, Fe 0.15
Lead, Pb 0.09
Phosphorous, P 0.05-0.4
Zinc, Zn Remainder

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
(Logout)
Your comment type
Submit

Editorial Highlights

Sponsored Content

Newsletters you may be interested in

See all Newsletters »

Terms

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.

Provide Feedback