Lead - An Introduction

Material: Lead - An Introduction
Composition: >99.9Pb typically
Property Minimum Value (S.I.) Maximum Value (S.I.) Units (S.I.) Minimum Value (Imp.) Maximum Value (Imp.) Units (Imp.)
Atomic Volume (average) 0.0182 0.0183 m3/kmol 1110.63 1116.73 in3/kmol
Density 11.31 11.39 Mg/m3 706.061 711.055 lb/ft3
Energy Content 29 54 MJ/kg 3141.82 5850.29 kcal/lb
Bulk Modulus 30 45 GPa 4.35113 6.52669 106 psi
Compressive Strength 4 12 MPa 0.580151 1.74045 ksi
Ductility 0.3 0.6 0.3 0.6 NULL
Elastic Limit 4 12 MPa 0.580151 1.74045 ksi
Endurance Limit 2 9 MPa 0.290075 1.30534 ksi
Fracture Toughness 5 15 MPa.m1/2 4.55023 13.6507 ksi.in1/2
Hardness 30 65 MPa 4.35113 9.42746 ksi
Loss Coefficient 0.065 0.14 0.065 0.14 NULL
Modulus of Rupture 4 12 MPa 0.580151 1.74045 ksi
Poisson's Ratio 0.435 0.445 0.435 0.445 NULL
Shear Modulus 4 6 GPa 0.580151 0.870226 106 psi
Tensile Strength 12 20 MPa 1.74045 2.90075 ksi
Young's Modulus 13 15 GPa 1.88549 2.17557 106 psi
Glass Temperature K °F
Latent Heat of Fusion 22 26.5 kJ/kg 9.45825 11.3929 BTU/lb
Maximum Service Temperature 293 323 K 67.73 121.73 °F
Melting Point 595 601 K 611.33 622.13 °F
Minimum Service Temperature 0 0 K -459.67 -459.67 °F
Specific Heat 122 135 J/kg.K 0.0944107 0.104471 BTU/lb.F
Thermal Conductivity 33 36 W/m.K 61.7771 67.3932 BTU.ft/h.ft2.F
Thermal Expansion 28.5 30 10-6/K 51.3 54 10-6/°F
Breakdown Potential MV/m V/mil
Dielectric Constant NULL
Resistivity 20.2 21 10-8 ohm.m 20.2 21 10-8 ohm.m
Environmental Properties
  Resistance Factors
1=Poor 5=Excellent
Flammability 5
Fresh Water 5
Organic Solvents 5
Oxidation at 500C 1
Sea Water 5
Strong Acid 3
Strong Alkalis 4
UV 5
Wear 3
Weak Acid 4
Weak Alkalis 5

This data is provided subject to AZoM.com's terms and conditions. Data reproduced with permission of Granta Design Limited www.grantadesign.com

Sponsored Content

Editorial Highlights

The Current State of the Global Semiconductor Market

The Current State of the Global Semiconductor Market

The global semiconductor market has entered an exciting period. Demand for chip technology is both driving the industry as well as hindering it, with current chip shortages predicted to last for some time. Current trends will likely shape the future of the industry, which is set to continue to show

How are Graphene Batteries Made?

How are Graphene Batteries Made?

The primary distinction between graphene-based batteries and solid-state batteries lies in the composition of either electrode. Although the cathode is commonly changed, carbon allotropes can also be employed in fabricating anodes.

Terms

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.

Provide Feedback