Sep 27 2012
The table below contains the chemical composition for copper alloys
C14200-C18500.
UNS |
Cu |
P |
Zr |
S |
Te |
Cd |
As |
Al |
Fe |
Mn |
Mg |
Ag |
C14200 |
99.68 |
0.02 |
- |
- |
- |
- |
0.3 |
- |
- |
- |
- |
- |
C14300 |
99.9 |
- |
- |
- |
- |
0.1 |
- |
- |
- |
- |
- |
- |
C14310 |
99.8 |
- |
- |
- |
- |
0.2 |
- |
- |
- |
- |
- |
- |
C14500 |
99.5 |
0.0040 -0.012 |
- |
- |
0.4-0.6 |
- |
- |
- |
- |
- |
- |
- |
C14700 |
99.6 |
- |
- |
0.2-0.5 |
- |
- |
- |
- |
- |
- |
- |
- |
C15000 |
99.85 |
- |
0.13-0.20 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C15100 |
99.9 |
- |
0.05-0.15 |
- |
- |
- |
- |
0.005 |
0.005 |
0.005 |
- |
- |
C15500 |
99.75 |
0.04-0.08 |
- |
- |
- |
- |
- |
- |
- |
- |
0.08-0.13 |
0.027-0.1 |
C15710 |
99.69-99.85 |
- |
- |
- |
- |
- |
- |
- |
0.010 |
- |
- |
- |
C15720 |
99.49-99.6 |
- |
- |
- |
- |
- |
- |
- |
0.010 |
- |
- |
- |
C15735 |
99.19-99.35 |
- |
- |
- |
- |
- |
- |
- |
0.010 |
- |
- |
- |
C15760 |
98.9 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C16200 |
98.78-99.3 |
- |
- |
- |
- |
0.70-1.20 |
- |
- |
0.020 |
- |
- |
- |
C16500 |
98.6 |
- |
- |
- |
- |
0.70-1.20 |
- |
- |
0.020 |
- |
- |
- |
C17000 |
98.1 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C18200 |
90-99.4 |
- |
- |
- |
- |
- |
- |
- |
0.1 |
- |
- |
- |
C18400 |
99.2 |
0.05 |
- |
- |
- |
- |
0.005 |
- |
0.15 |
- |
- |
- |
C18500 |
99.3 |
0.04 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
0.08-0.12 |
UNS |
Ag |
Pb |
Other |
Zn |
O |
Sn |
Be |
Co+Ni |
Co+Ni+Fe |
Cr |
Si |
Ca |
Li |
Other |
C14200 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C14300 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C14310 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C14500 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C14700 |
- |
- |
0.1 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C15000 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C15100 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C15500 |
0.027-0.1 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C15710 |
- |
0.010 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
0.15-0.25 |
C15720 |
- |
0.010 |
- |
- |
0.040 |
- |
- |
- |
- |
- |
- |
- |
- |
0.35-0.45 |
C15735 |
- |
0.010 |
- |
- |
0.040 |
- |
- |
- |
- |
- |
- |
- |
- |
0.65-0.75 |
C15760 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
1.1 |
C16200 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
C16500 |
- |
- |
- |
- |
- |
0.6 |
- |
- |
- |
- |
- |
- |
- |
- |
C17000 |
- |
- |
- |
- |
- |
- |
1.60-1.79 |
0.2 |
0.6 |
- |
- |
- |
- |
- |
C18200 |
- |
0.05 |
0.5 |
- |
- |
- |
- |
- |
- |
0.60-1.20 |
0.1 |
- |
- |
- |
C18400 |
- |
- |
0.2 |
0.7 |
- |
- |
- |
- |
- |
0.4-1.20 |
0.1 |
0.005 |
0.05 |
- |
C18500 |
0.08-0.12 |
0.015 |
- |
- |
- |
- |
- |
- |
- |
0.4-1 |
- |
- |
0.04 |
- |