Sep 20 2012
Oxygen free copper UNS C10300 has a copper content of not less than 99.95% copper. Tabulated below are the mechanical properties of UNS C10300 tubes as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str |
Fatigue Str. |
B |
C |
F |
30T |
H55 |
1.65mm (0.065in) |
276MPa (40ksi) |
221MPa (32ksi) |
25% |
35 |
- |
77 |
45 |
179MPa (26ksi) |
- |
H80 |
1.65mm (0.065in) |
379MPa (55ksi) |
345MPa (50ksi) |
8% |
60 |
- |
95 |
63 |
200MPa (29ksi) |
- |
OS025 |
1.65MPa (0.065in) |
234MPa (34ksi) |
76MPa (11ksi) |
45% |
- |
- |
45 |
- |
159MPa (23ksi) |
- |
OS050 |
1.65MPa (0.065in) |
221MPa (32ksi) |
69MPa (10ksi) |
45% |
- |
- |
40 |
- |
152MPa (22ksi) |
- |
Equivalent materials to UNS C10300 copper alloy are given in the table below.
ASTM B111 |
ASTM B133 |
ASTM B152 |
ASTM B187 |
ASTM B188 |
ASTM B224 |
ASTM B280 |
ASTM B302 |
ASTM B306 |
ASTM B359 |
ASTM B372 |
ASTM B379 |
ASTM B395 |
ASTM B42 |
ASTM B432 |
ASTM B447 |
ASTM B638 |
ASTM B640 |
ASTM B641 |
ASTM B68 |
ASTM B687 |
ASTM B698 |
ASTM B716 |
ASTM B743 |
ASTM B75 |
ASTM B88 |
MIL B-20292 |
MIL T-3235 |
|
|
|
|
|
|
|