Oxygen free copper UNS C10400 has a copper content of not less than 99.95% copper.
The following table shows the mechanical properties of UNS C10400 wires as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Elong. |
Shear Str |
H04 |
2mm. (0.08 in.) |
379MPa (55ksi) |
1% |
200MPa (29ksi) |
H08 |
2mm. (0.08 in.) |
445MPa (66ksi) |
1% |
228MPa (33ksi) |
OS050 |
2mm. (0.08 in.) |
241MPa (35ksi) |
35% |
165MPa (24ksi) |
Equivalent materials to UNS C10400 copper alloy are given in the table below.
MIL W-3318 |
MIL B-20292 |
ASTM B506 |
ASTM B49 |
ASTM B355 |
ASTM B3 |
ASTM B298 |
ASTM B272 |
ASTM B246 |
ASTM B224 |
ASTM B2 |
ASTM B189 |
ASTM B188 |
ASTM B187 |
ASTM B152 |
ASTM B133 |
ASTM B1 |
ASME SB152 |
|
|
|
|
|
|
|
|