Sep 27 2012
Electrolytic tough pitch copper UNS C11000 has a copper content of not less than 99.90%.
The following table shows the mechanical properties of UNS C11000 shapes as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
B |
C |
F |
30T |
M20 |
12.7mm (0.5in) |
221MPa (32ksi) |
69MPa (10ksi) |
50% |
- |
- |
40 |
- |
152MPa (22ksi) |
M30 |
12.7mm (0.5in) |
221MPa (32ksi) |
69MPa (10ksi) |
50% |
- |
- |
40 |
- |
152MPa (22ksi) |
OS050 |
12.7mm (0.5in) |
221MPa (32ksi) |
69MPa (10ksi) |
50% |
- |
- |
40 |
- |
152MPa (22ksi) |
Equivalent materials to UNS C11000 copper alloy are the following.
ASME SB133 |
ASTM B173 |
ASTM B228 |
ASTM B33 |
ASTM B49 |
ASTM F467 |
ASTM B1 |
ASTM B174 |
ASTM B229 |
ASTM B355 |
ASTM B496 |
ASTM F468 |
ASTM B101 |
ASTM B187 |
ASTM B246 |
ASTM B370 |
ASTM B506 |
MIL B-20292 |
ASTM B116 |
ASTM B188 |
ASTM B272 |
ASTM B447 |
ASTM B556 |
MIL C-12168 |
ASTM B124 |
ASTM B189 |
ASTM B283 |
ASTM B451 |
ASTM B638 |
MIL W-6712 |
ASTM B133 |
ASTM B2 |
ASTM B286 |
ASTM B47 |
ASTM B694 |
QQ B575 |
ASTM B152 |
ASTM B224 |
ASTM B298 |
ASTM B470 |
ASTM B738 |
SAE J461 |