UNS C15500 has a copper content of not less than 99.75% copper.
The following table shows the mechanical properties of UNS C15500 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Fatigue Str. |
B |
C |
F |
30T |
H01 |
1mm. (0.04 in.) |
310MPa (45ksi) |
248MPa (36ksi) |
25% |
- |
- |
89 |
- |
- |
|
5.08mm. (0.2 in.) |
310MPa (45ksi) |
248MPa (36ksi) |
28% |
- |
- |
89 |
- |
- |
H02 |
1mm. (0.04 in.) |
365MPa (53ksi) |
324MPa (47ksi) |
13% |
- |
- |
92 |
- |
- |
H04 |
1mm. (0.04 in.) |
427MPa (62ksi) |
393MPa (57ksi) |
5% |
- |
- |
97 |
- |
162MPa (24ksi) |
H08 |
1mm. (0.04 in.) |
462MPa (67ksi) |
448MPa (65ksi) |
4% |
- |
- |
100 |
- |
155MPa (23ksi) |
H10 |
1mm. (0.04 in.) |
496MPa (72ksi) |
469MPa (68ksi) |
3% |
80 |
- |
- |
- |
- |
H12 |
1mm. (0.04 in.) |
517MPa (75ksi) |
483MPa (70ksi) |
3% |
82 |
- |
- |
- |
- |
H14 |
1mm. (0.04 in.) |
552MPa (80ksi) |
496MPa (72ksi) |
3% |
84 |
- |
- |
- |
- |
O50 |
1mm. (0.04 in.) |
276MPa (40ksi) |
124MPa (18ksi) |
34% |
- |
- |
70 |
- |
103MPa (15ksi) |
|
5.08mm. (0.2 in.) |
276MPa (40ksi) |
124MPa (18ksi) |
40% |
- |
- |
70 |
- |
- |
Equivalent material to UNS C15500 copper alloy is ASTM B888.