Sep 27 2012
UNS C16200 cadmium copper alloy has a copper content of not less than 99%.
The following table outlines the mechanical properties of UNS C16200 rods as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str |
Fatigue Str. |
B |
C |
F |
30T |
H04 |
12.7 mm (0.5 in) |
503 MPa (73 ksi) |
474 MPa (69 ksi) |
9% |
73 |
- |
- |
- |
386 MPa (56 ksi) |
207 MPa (30 ksi) |
OS025 |
12.7 mm (0.5 in) |
248 MPa (36 ksi) |
83 MPa (12 ksi) |
57% |
- |
- |
46 |
- |
- |
- |
OS050 |
12.7 mm (0.5 in) |
241 MPa (35 ksi) |
48 MPa (7 ksi) |
56% |
- |
- |
46 |
- |
186 MPa (27 ksi) |
100 MPa (15 ksi) |
Equivalent materials to UNS C16200 copper alloy include:
- ASTM B105
- SAE J461
- SAE J463