UNS C26200 copper alloy has a copper content of not less than 67%.
The following table shows the mechanical properties of UNS C26200 wires as a function of heat treatment and thickness.
| Temper |
Thickness |
Tensile Str. |
Elong |
Shear Str. |
Fatigue Str. |
| H00 |
2 mm (0.08 in) |
400 MPa (58 ksi) |
35% |
262 MPa (32 ksi) |
- |
| H01 |
2 mm (0.08 in) |
483 MPa (70 ksi) |
20% |
- |
- |
| H06 |
2 mm (0.08 in) |
855 MPa (124 ksi) |
4% |
- |
- |
| H08 |
2 mm (0.08 in) |
896 MPa (130 ksi) |
3% |
414 MPa (60 ksi) |
152 MPa (22 ksi) |
| OS015 |
2 mm (0.08 in) |
372 MPa (54 ksi) |
56% |
- |
- |
| OS025 |
2 mm (0.08 in) |
359 MPa (52 ksi) |
58% |
- |
- |
| OS035 |
2 mm (0.08 in) |
345 MPa (50 ksi) |
60% |
234 MPa (34 ksi) |
- |
| OS050 |
2 mm (0.08 in) |
331 MPa (48 ksi) |
64% |
- |
- |
The chemical composition of copper alloy is outlined in the following table.
| Element |
Content (%) |
| Copper, Cu |
67-70 |
| Lead Pb |
0.07 |
| Iron, Fe |
0.05 |
| Zinc, Zn |
Remainder |