UNS C16500 has a copper content of not less than 98.6%.
Tabulated below are the mechanical properties of UNS C16500 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
H04 |
1mm (0.04in) |
455MPa (66ksi) |
- |
5% |
79 |
- |
- |
- |
H06 |
1mm (0.04in) |
476MPa (69ksi) |
452MPa (66ksi) |
2% |
- |
- |
- |
67 |
H08 |
1mm (0.04in) |
503MPa (73ksi) |
455MPa (66ksi) |
2% |
- |
- |
- |
72 |
H10 |
1mm (0.04in) |
524MPa (76ksi) |
476MPa (69ksi) |
1% |
- |
- |
- |
73 |
The chemical composition of UNS C16500 copper alloy is outlined in the following table.
Elements |
Content (%) |
Cadmium, Cd |
0.6-1.0 |
Tin, Sn |
0.50-.7 |
Iron, Fe |
0.02 |
Copper, Cu |
Remainder |
Equivalent materials to UNS C16500 copper alloy are: