Nov 23 2012
The following table shows the mechanical properties of UNS C17500 rods as a function of heat treatment.
Temper |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
TB00 |
310MPa (45ksi) |
172MPa (25ksi) |
28% |
35 |
- |
- |
- |
TD04 |
496MPa (72ksi) |
448MPa (65ksi) |
12% |
68 |
- |
- |
- |
TF00 |
758MPa (110ksi) |
621MPa (90ksi) |
18% |
96 |
- |
- |
8 |
TH04 |
793MPa (115ksi) |
758MPa (110ksi) |
14% |
98 |
- |
- |
- |
Equivalent materials to UNS C17500 copper alloy are the following:
- ASTM B441
- ASTM B534
- MIL C-81021
- SAE J461
- SAE J463
The chemical composition of UNS C17500 copper alloy is outlined in the following table.
Element |
Content (%) |
Cobalt, Co |
2.4-2.7 |
Beryllium, Be |
0.4-0.7 |
Silicon, Si |
0.2 |
Aluminum. Al |
0.2 |
Iron, Fe |
0.1 |
Copper, Cu |
Remainder |
Copper and the elements mentioned in the above table together constitute 99.5% of this alloy.