Copper UNS C12510 has a copper content of not less than 99.9%.
The following table shows the mechanical properties of UNS C12510 flat products as a function of heat treatment and thickness.
| Temper |
Thickness |
Tensile Str. |
Elong. |
| H01 |
0.076mm (0.03in) |
276MPa (40ksi) |
5% |
|
0.5mm (0.02in) |
276MPa (40ksi) |
23% |
| H02 |
0.076mm (0.03in) |
310MPa (45ksi) |
2% |
|
0.5mm (0.02in) |
310MPa (45ksi) |
12% |
| H03 |
0.076mm (0.03in) |
310MPa (48ksi) |
2% |
|
0.5mm (0.02in) |
310MPa (48ksi) |
6% |
| H04 |
0.076mm (0.03in) |
352MPa (51ksi) |
1% |
|
0.5mm (0.02in) |
352MPa (51ksi) |
3% |
| H06 |
0.076mm (0.03in) |
379MPa(55ksi) |
15% |
|
0.5mm (0.02in) |
379MPa(55ksi) |
40% |
| H08 |
0.076mm (0.03in) |
407MPa (59ksi) |
0% |
|
0.5mm (0.02in) |
407MPa (59ksi) |
1% |
| H10 |
0.076mm (0.03in) |
407MPa (59ksi) |
0% |
|
0.5mm (0.02in) |
407MPa (59ksi) |
1% |
| OS015 |
0.076mm (0.03in) |
228MPa (33ksi) |
45% |
|
0.5mm (0.02in) |
228MPa (33ksi) |
50% |