Copper UNS C15100 has a copper content of not less than 99.8%.
The following table shows the mechanical properties of UNS C15100 flat products as a function of heat treatment and thickness.
| Temper |
Thickness |
Tensile Str. |
Elong. |
Rockwell |
| B |
C |
F |
30T |
| H01 |
1.02mm (0.04in) |
290MPa (42ksi) |
13% |
30 |
- |
81 |
48 |
| H02 |
1.02mm (0.04in) |
324MPa (47ksi) |
9% |
37 |
- |
87 |
56 |
| H03 |
1.02mm (0.04in) |
352MPa (51ksi) |
6% |
47 |
- |
90 |
59 |
| H04 |
1.02mm (0.04in) |
393MPa (57ksi) |
4% |
57 |
- |
59 |
61 |
| H06 |
1.02mm (0.04in) |
434MPa (63ksi) |
4% |
57 |
- |
59 |
61 |
| H08 |
1.02mm (0.04in) |
469MPa (68ksi) |
2% |
64 |
- |
- |
65 |
| OS015 |
1.02mm (0.04in) |
262MPa (38ksi) |
36% |
47 |
- |
- |
- |
An equivalent material to UNS C15100 copper alloy is ASTM B747.