Sep 27 2012
Phosphor Bronze UNS C51000 has a copper content of not less than 94%.
The following table shows the mechanical properties of UNS C51000 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Fatigue Str. |
B |
C |
F |
30T |
H01 |
- |
340MPa (49ksi) |
- |
24% |
- |
- |
- |
- |
- |
H02 |
- |
455MPa (66ksi) |
- |
24% |
78 |
- |
- |
69 |
- |
H04 |
1mm (0.04in) |
579MPa (84ksi) |
- |
7% |
87 |
- |
- |
75 |
172MPa (25ksi) |
H06 |
1mm (0.04in) |
662MPa (96ksi) |
- |
3% |
93 |
- |
- |
78 |
- |
H08 |
1mm (0.04in) |
710MPa (103ksi) |
- |
3% |
95 |
- |
- |
79 |
152MPa (22ksi) |
H10 |
1mm (0.04in) |
738MPa (107ksi) |
- |
2% |
97 |
|
|
80 |
- |
HR02 |
- |
455MPa (66ksi) |
- |
28% |
- |
- |
- |
- |
- |
HR04 |
- |
579MPa (84ksi) |
- |
14% |
- |
- |
- |
- |
- |
HR06 |
- |
662MPa (96ksi) |
- |
11% |
- |
- |
- |
- |
- |
HR08 |
- |
710MPa (103ksi) |
- |
9% |
- |
- |
- |
- |
- |
M20 |
- |
345MPa (50ksi) |
- |
- |
- |
- |
- |
- |
- |
O60 |
- |
345MPa (50ksi) |
- |
- |
40 |
- |
- |
- |
- |
O61 |
- |
315MPa (46ksi) |
- |
- |
47 |
- |
- |
- |
- |
OS015 |
1mm (0.04in) |
365MPa (53ksi) |
152MPa (22ksi) |
50% |
34 |
- |
79 |
- |
- |
OS025 |
1mm (0.04in) |
345MPa (50ksi) |
145MPa (21ksi) |
52% |
30 |
- |
77 |
- |
- |
OS035 |
1mm (0.04in) |
338MPa (49ksi) |
138MPa (20ksi) |
58% |
28 |
- |
75 |
- |
- |
OS050 |
1mm (0.04in) |
324MPa (47ksi) |
131MPa (19ksi) |
64% |
26 |
- |
73 |
- |
- |
Equivalent materials to UNS C51000 copper alloy are the following:
- AMS 4720
- ASTM B100
- ASTM B103
- ASTM B139
- ASTM B159
- ASTM F467
- ASTM F468
- MIL B-13501
- MIL W-6712
- QQ W321
- SAE J461
- SAE J463
The chemical composition of UNS C51000 copper alloy is outlined in the following table.
Element |
Content (%) |
Tin, Sn |
4.2-5.8 |
Zinc, Zn |
0.3 |
Iron, Fe |
0.1 |
Lead, Pb |
0.05 |
Phosphorous, P |
0.03-0.35 |
Copper, Cu |
Balance |