UNS C61500 has a copper content of not less than 90%.
Tabulated below are the mechanical properties of UNS C61500 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
H02 |
1mm (0.04in) |
724MPa (105ksi) |
15% |
- |
- |
- |
81 |
H04 |
1mm (0.04in) |
862MPa (125ksi) |
5% |
- |
- |
- |
83 |
H06 |
1mm (0.04in) |
931MPa (135ksi) |
4% |
- |
- |
- |
84 |
H08 |
1mm (0.04in) |
965MPa (140ksi) |
3% |
- |
- |
- |
85 |
O50 |
1mm (0.04in) |
586MPa (85ksi) |
36% |
- |
- |
- |
70 |
O60 |
1mm (0.04in) |
483MPa (70ksi) |
55% |
- |
- |
- |
42 |
The chemical composition of UNS C61500 copper alloy is outlined in the following table.
Elements |
Content (%) |
Al |
7.7-8.3 |
Ni |
1.8-2.2 |
Pb |
0.015 |
Cu |
Remainder |