Aluminum bronze UNS C63200 has a copper content of not less than 82%.
The following table shows the mechanical properties of UNS C63200 rod as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
O50 |
25.4 mm. (1 in.) |
724MPa (105ksi) |
365MPa (53ksi) |
22% |
96 |
- |
- |
- |
|
51 mm. (2 in.) |
710MPa (103ksi) |
359MPa (52ksi) |
24% |
92 |
- |
- |
- |
|
76 mm. (3 in.) |
703MPa (1025ksi) |
352MPa (51ksi) |
24% |
93 |
- |
- |
- |
Equivalent materials to UNS C63200 copper alloy are provided in the table below.
-
ASTM B124
-
ASTM B150
-
ASTM B283
The chemical composition of UNS C63200 copper alloy is outlined in the following table.
Element |
Content (%) |
Aluminum, Al |
8.7-9.5 |
Nickel, Ni |
4.0-4.8 |
Iron, Fe |
3.5-4.3 |
Manganese, Mn |
1.2-2.0 |
Silicon, Si |
0.1 |
Lead, Pb |
0.02 |
Copper, Cu |
Balance |