Nov 26 2012
UNS C35600 extra high leaded brass has a copper content of not less than 60%.
The following table shows the mechanical properties of UNS C35600 flat products as a function of heat treatment and thickness.
|
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
|
B |
C |
F |
30T |
|
H01 |
1 mm (0.04 in) |
372 MPa (54 ksi) |
276 MPa (40 ksi) |
35% |
55 |
- |
- |
54 |
|
H02 |
1 mm (0.04 in) |
421 MPa (61 ksi) |
345 MPa (50 ksi) |
20% |
70 |
- |
- |
65 |
|
H04 |
1 mm (0.04 in) |
510 MPa (74 ksi) |
448 MPa (65 ksi) |
8% |
81 |
- |
- |
- |
|
H06 |
1 mm (0.04 in) |
607 MPa (88 ksi) |
455 MPa (66 ksi) |
5% |
85 |
- |
- |
- |
|
H08 |
1 mm (0.04 in) |
634 MPa (92 ksi) |
462 MPa (67 ksi) |
4% |
87 |
- |
- |
- |
|
H10 |
1 mm (0.04 in) |
669 MPa (97 ksi) |
469 MPa (68 ksi) |
3% |
89 |
- |
- |
- |
|
OS015 |
1 mm (0.04 in) |
372 MPa (54 ksi) |
221 MPa (33 ksi) |
42% |
52 |
- |
- |
86 |
|
OS035 |
1 mm (0.04 in) |
338 MPa (49 ksi) |
117 MPa (17 ksi) |
50 |
- |
- |
68 |
31 |
|
OS050 |
1 mm (0.04 in) |
324 Ma (47 ksi) |
110 MPa (16 ksi) |
60% |
12 |
- |
62 |
- |
The chemical composition of UNS C35600 copper alloy is outlined in the following table.
|
Element |
Content (%) |
|
Copper, Cu |
60-63 |
|
Lead, Pb |
2.0-3.0 |
|
Lead, Pb |
0.15 |
|
Zinc, Zn |
Remainder |
Equivalent materials to UNS C35600 copper alloy are: