Polyurethane - Semi-Rigid Foam

Advantages

Higher flexural modulus, maximum operating temperature and HDT compared with soft microcellular polyurethane.

Disadvantages

Lowest notched impact strength and tensile strength compared with other thermosetting polyurethane’s contained within Plascams.

Typical Properties

Property

Value

Density (g/cm3).

0.8

Surface Hardness

SA70

Tensile Strength (MPa)

4

Flexural Modulus (GPa)

0.01

Notched Izod (kJ/m)

0.4

Linear Expansion (/°C x 10-5)

11

Elongation at Break (%)

150

Strain at Yield (%)

N/Y

Max. Operating Temp. (°C)

80

Water Absorption (%)

0.4

Oxygen Index (%)

24

Flammability UL94

HB

Volume Resistivity (log ohm.cm)

12

Dielectric Strength (MV/m)

16

Dissipation Factor1kHz

0.003

Dielectric Constant  1kHz

4

HDT @ 0.45 MPa (°C)

20-

HDT @ 1.80 MPa (°C)

30

Material Drying  hrs @ °C

NA

Melting Temp. Range (°C)

NA

Mould Shrinkage (%)

1.7

Mould Temp. Range (°C)

NA

Applications

Insulation, foam-in-place buoyancy.

 

Source : Abstracted from Plascams

For more information on Plascams please visit The Rubber and Plastics Research Association

 

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.