Flat Products (UNS C63800) - Mechanical Properties

UNS C63800 has a copper content of not less than 95%.

The following table shows the mechanical properties of UNS C63800 flat products as a function of heat treatment and thickness.

Temper Thickness Tensile Str. Yield Str. Elong. Rockwell Fatigue Str.
B C F 30T
H01 1mm. (0.04 in.) 662MPa (96ksi - 23% 93 - - 78 -
H02 1mm. (0.04 in.) 731MPa (106ksi) - 15% 96 - - 79 -
H04 1mm. (0.04 in.) 827MPa (120ksi) - 7% 79 - - 82 -
H06 1mm. (0.04 in.) 855MPa (124ksi) - 5% 100 - - 82 -
H08 1mm. (0.04 in.) 883MPa (128ksi) - 4% 101 - - 82 241MPa (35ksi)
H10 1mm. (0.04 in.) 896MPa (130ksi) - 4% 101 - - 83 -
O60 1mm. (0.04 in.) 565MPa (82ksi) 365MPa (53ksi) 36% 86 - - 73 -

Equivalent material to UNS C63800 copper alloy is given ASTM B422.

The chemical composition of UNS C63000 copper alloy is outlined in the following table.

Element Content (%)
Aluminum, Al 2.5-3.1
Silicon, Si 1.5-2.1
Zinc, Zn 0.8
Cobalt, Co 0.25-0.55
Nickel, Ni 0.20
Iron, Fe 0.20
Manganese, Mn 0.10
Lead, Pb 0.05
Copper, Cu Remainder

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.