Jan 23 2013
Copper-bismuth-selenium UNS C89530 has a copper content of not less than 84%.
The following table shows the mechanical properties of UNS C89530 sand cast alloy as a function of heat treatment.
Temper |
Tensile Str. |
Elong. |
Shear Str. |
Fatigue Str. |
M01 |
195MPa (28ksi) |
15% |
- |
- |
|
230MPa (33ksi) |
- |
12MPa (1ksi) |
70MPa (10ksi) |
|
260MPa (38ksi) |
- |
- |
- |
The chemical composition of UNS C89530 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
84-89 |
Zinc, Zn |
7-9 |
Tin, Sn |
3.5-6.0 |
Bismuth, Bi |
1-2 |
Nickel, Ni |
1 |
Iron, Fe |
0.3 |
Lead, Pb |
0.2 |
Antimony, Sb |
0.2 |
Selenium, Se |
0.10-0.30 |
Phosphorus, P |
0.05 |
Aluminum, Al |
0.01 |
Silicon, Si |
0.01 |