Perfluoroalkoxyethylene - PFA 20% Glass Fibre Reinforced

Sep 5 2001

Polymer Type

Thermoplastic

Advantages

Significant increase in HDT and moderate increase in tensile strength compared with unmodified grades of PFA.

Disadvantages

Decreased elongation at break and notched izod impact strength compared with unmodified grades of PFA.

Typical Properties

Property

Value

Density (g/cm3)

2.24

Surface Hardness

SD68

Tensile Strength (MPa)

33

Flexural Modulus (GPa)

0.7

Notched Izod (kJ/m)

0.7

Linear Expansion  (/°C x 10-5)

13.6

Elongation at Break (%)

4

Strain at Yield (%)

N/Y

Max. Operating Temp. (°C)

170

Water Absorption (%)

0.04

Oxygen Index (%)

95

Flammability UL94

V0

Volume Resistivity (log ohm.cm)

18

Dielectric Strength (MV/m)

40

Dissipation Factor 1kHz

0.001

Dielectric Constant  1kHz

2.9

HDT @ 0.45 MPa (°C)

160

HDT @ 1.80 MPa (°C)

150

Material. Drying  hrs @ (°C)

NA

Melting Temp. Range (°C)

360 - 420

Mould Shrinkage (%)

0.8

Mould Temp. Range (°C)

50 - 250

Applications

Chemical plants.

 

Source : Abstracted from Plascams

For more information on Plascams please visit RAPRA Technology Ltd.

 

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
(Logout)
Your comment type
Submit

Sponsored Content

Editorial Highlights

The Current State of the Global Semiconductor Market

The Current State of the Global Semiconductor Market

The global semiconductor market has entered an exciting period. Demand for chip technology is both driving the industry as well as hindering it, with current chip shortages predicted to last for some time. Current trends will likely shape the future of the industry, which is set to continue to show

How are Graphene Batteries Made?

How are Graphene Batteries Made?

The primary distinction between graphene-based batteries and solid-state batteries lies in the composition of either electrode. Although the cathode is commonly changed, carbon allotropes can also be employed in fabricating anodes.

Newsletters you may be interested in

See all Newsletters »