Beryllium Copper Rod UNS C17460 - Mechanical Properties

Sep 27 2012

The following table shows the mechanical properties of UNS C17460 rod as a function of heat treatment and thickness.

Temper Thickness Tensile Str. Elong. Rockwell
B C F 30T
TH04 4.8mm (0.188in) 896MPa (130ksi) 12% 103 - - -

The chemical composition of UNS C17460 copper alloy is outlined in the following.

Elements Content (%)
Nickel, Ni 1-1.4
Zirconium, Zr 0.5
Tin, Sn 0.25
Aluminum, Al 0.2
Silicon, Si 0.2
Iron. Fe 0.2
Beryllium, Be 0.15-0.50
Copper, Cu Balance

Copper and the elements mentioned in the above table together constitute 99.5% of this alloy.

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
(Logout)
Your comment type
Submit

Editorial Highlights

What are Metamaterials?

What are Metamaterials?

Explore how metamaterials are redefining science and engineering, from earthquake-resistant materials to adaptive aircraft and soft robotics. Smarter, stronger, and more responsive technologies for the next generation.

Sponsored Content

Newsletters you may be interested in

See all Newsletters »

Terms

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.

Provide Feedback