Polyester - Vinyl Ester

Sponsored by Dotmar EPP Pty LtdAug 16 2001

Higher maximum operating temperature and oxygen index, and significantly lower mould shrinkage compared with rigid casting polyester.

Disadvantages

Lower flexural modulus and HDT than rigid casting polyester.

Property	Value
Density (g/cm³)	1.05
Surface Hardness	RM80
Tensile Strength (MPa)	60
Flexural Modulus (GPa)	3
Notched Izod (kJ/m)	0.02
Linear Expansion (/°C x 10^-5)	7.5
Elongation at Break (%)	5
Strain at Yield (%)	N/A
Max. Operating Temp. (°C)	140
Water Absorption (%)	0.2
Oxygen Index (%)	24
Flammability UL94	V1
Volume Resistivity (log ohm.cm)	15
Dielectric Strength (MV/m)	16
Dissipation Factor1kHz	0.015
Dielectric Constant 1kHz	4.5
HDT @ 0.45 MPa (°C)	90
HDT @ 1.80 MPa (°C)	75
Material Drying hrs @ °C	NA
Melting Temp. Range (°C)	20 - 50
Mould Shrinkage (%)	0.25
Mould Temp. Range (°C)	130 - 150

Absorption towers, process vessels, storage tanks, piping, hood scrubbers, ducts and exhaust stacks.

This information has been sourced, reviewed and adapted from materials provided by Dotmar EPP Pty Ltd.

For more information on this source, please visit Dotmar EPP Pty Ltd.

Please use one of the following formats to cite this article in your essay, paper or report:

APA
Dotmar EPP Pty Ltd. (2019, April 29). Polyester - Vinyl Ester. AZoM. Retrieved on December 02, 2020 from https://www.azom.com/article.aspx?ArticleID=703.
MLA
Dotmar EPP Pty Ltd. "Polyester - Vinyl Ester". AZoM. 02 December 2020. <https://www.azom.com/article.aspx?ArticleID=703>.
Chicago
Dotmar EPP Pty Ltd. "Polyester - Vinyl Ester". AZoM. https://www.azom.com/article.aspx?ArticleID=703. (accessed December 02, 2020).
Harvard
Dotmar EPP Pty Ltd. 2019. Polyester - Vinyl Ester. AZoM, viewed 02 December 2020, https://www.azom.com/article.aspx?ArticleID=703.