Copper Sand Cast Alloy (UNS C95500) - Mechanical Properties

UNS C95500 has a copper content of not less than 78%.

Tabulated below are the mechanical properties of UNS C95500 sand cast alloy as a function of heat treatment.

Temper Tensile Str. Yield Str. Elong. Rockwell Shear Str. Fatigue Str.
B C F 30T
M01 689MPa (100ksi) 303MPa (44ksi) 12% 87 - - - 331MPa (48ksi) 214MPa (31ksi)
620MPa (90ksi) 275MPa (40ksi) 6% - - - - - -
TQ50 827MPa (120ksi) 469MPa (68ksi) 10% - - - - 483MPa (70ksi) 262MPa (38ksi)
760MPa (110ksi) 415MPa (60ksi) 5% - - - - - -

The chemical composition of UNS C95500 copper alloy is outlined in the following table.

Elements Content (%)
Copper, Cu 78
Aluminum, Al 10.0-11.5
Manganese, Mn 3.5
Nickel, Ni 3.0-5.5
Iron, Fe 3.0-5.0

Equivalent materials to UNS C95500 copper alloy are given in the table below.

  • ASTM B148
  • ASTM B271
  • ASTM B30
  • ASTM B505
  • ASTM B763
  • ASTM B806
  • QQ C390
  • SAE J461
  • SAE J462

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.