Titanium Alloys - Ti6Al2Sn4Zr6Mo

Material: Titanium Alloys - Ti6Al2Sn4Zr6Mo
Composition: Ti/6Al/2Sn/4Zr/6Mo
Property Minimum Value (S.I.) Maximum Value (S.I.) Units (S.I.) Minimum Value (Imp.) Maximum Value (Imp.) Units (Imp.)
Atomic Volume (average) 0.01 0.011 m3/kmol 610.237 671.261 in3/kmol
Density 4.64 4.66 Mg/m3 289.666 290.914 lb/ft3
Energy Content 750 1250 MJ/kg 81254 135423 kcal/lb
Bulk Modulus 125 148 GPa 18.1297 21.4656 106 psi
Compressive Strength 1120 1170 MPa 162.442 169.694 ksi
Ductility 0.1 0.2 0.1 0.2 NULL
Elastic Limit 1069 1100 MPa 155.045 159.542 ksi
Endurance Limit 633 646 MPa 91.8088 93.6943 ksi
Fracture Toughness 70 80 MPa.m1/2 63.7033 72.8037 ksi.in1/2
Hardness 3360 3510 MPa 487.327 509.083 ksi
Loss Coefficient 0.001 0.002 0.001 0.002 NULL
Modulus of Rupture 1120 1170 MPa 162.442 169.694 ksi
Poisson's Ratio 0.35 0.37 0.35 0.37 NULL
Shear Modulus 41 43 GPa 5.94655 6.23662 106 psi
Tensile Strength 1172 1200 MPa 169.984 174.045 ksi
Young's Modulus 113 115 GPa 16.3893 16.6793 106 psi
Glass Temperature K °F
Latent Heat of Fusion 360 370 kJ/kg 154.771 159.071 BTU/lb
Maximum Service Temperature 710 730 K 818.33 854.33 °F
Melting Point 1900 1916 K 2960.33 2989.13 °F
Minimum Service Temperature 0 K -459.67 °F
Specific Heat 540 650 J/kg.K 0.417883 0.503008 BTU/lb.F
Thermal Conductivity 6.9 7.1 W/m.K 12.917 13.2914 BTU.ft/h.ft2.F
Thermal Expansion 9.4 9.8 10-6/K 16.92 17.64 10-6/°F
Breakdown Potential MV/m V/mil
Dielectric Constant NULL
Resistivity 158 200 10-8 ohm.m 158 200 10-8 ohm.m
Environmental Properties
  Resistance Factors
1=Poor 5=Excellent
Flammability 5
Fresh Water 5
Organic Solvents 5
Oxidation at 500C 4
Sea Water 5
Strong Acid 4
Strong Alkalis 4
UV 5
Wear 3
Weak Acid 5
Weak Alkalis 5