Introduction
Copper casting alloy UNS C87500 is an alloy of copper and silicon. Brass is a preferred alloy for architecture. Brass has attractive color and can be moulded into different shapes.
The following datasheet provides chemical composition and properties of UNS C87500 alloy.
Chemical Composition
The chemical composition of UNS C87500 alloy is given in the following table.
Element |
Content (%) |
Cu |
82 |
Zn |
14 |
Si |
4 |
Physical Properties
The following table details the physical properties of UNS C87500 alloy.
Properties |
Metric |
Imperial |
Density |
8.28 g/cm3 |
0.299 lb/in³ |
Mechanical Properties
The mechanical properties of UNS C87500 alloy are shown in the following table.
Properties |
Metric |
Imperial |
Elastic modulus |
117 GPa |
16969 ksi |
Poisson's ratio |
0.34 |
0.34 |
Hardness, Brinell |
134 |
134 |
Hardness Rockwell B |
83 |
83 |
Tensile strength |
460 MPa |
66700 psi |
Yield strength |
205 MPa |
29700 psi |
Elongation at break |
21.00% |
21.00% |
Machinability |
50 |
50 |
Creep strength |
9.50 MPa |
1380 psi |
Compressive strength |
183 MPa |
26500 psi |
Charpy impact |
43.0 J |
31.7 ft.lb |
Fatigue strength |
150 MPa |
21800 psi |
Thermal properties
The following table discusses thermal properties of UNS C87500 alloy.
Properties |
Metric |
Imperial |
Thermal expansion co-efficient (@75°C/167°F) |
17.1 µm/m°C |
9.50 µin/in°F |
Thermal conductivity( @20°C/68°F) |
26.0 W/mK |
180 BTUin/hr.ft².°F |
Other Designations
Equivalent designations to UNS C87500 alloy include:
- ASTM B271
- ASTM B30
- ASTM B584
- ASTM B763
- ASTM B806
- QQ C390
- SAE J461
- SAE J462
Fabrication and Heat Treatment
Machinability
UNS C87500 alloy has a machinability rating of 50.
Welding
The preferred welding techniques for UNS C87500 alloy are brazing, oxyacetylene welding and gas shielded arc welding. Carbon arc welding, coated metal arc welding and soldering are not recommended for this alloy.