Written by AZoMSep 16 2001
| |
| |
Polymer Type |
| Thermoplastic |
Advantages |
| Good flexibility, abrasion resistance and notched izod impact strength compared with unmodified polyamide 12 plastics. |
Disadvantages |
| Reduced heat distortion temperature, increased coefficient of linear expansion and poor electrical characteristics compared with unmodified Polyamide 12. |
Typical Properties |
| | | Density (g/cm3) | 1.03 | | Surface Hardness | RR85 | | Tensile Strength (MPa) | 30 | | Flexural Modulus (GPa) | 0.55 | | Notched Izod (kJ/m) | 0.07 | | Linear Expansion (/°C x 10-5) | 12 | | Elongation at Break (%) | 300 | | Strain at Yield (%) | 30 | | Max. Operating Temp. (°C) | 70 | | Water Absorption (%) | 0.2 | | Oxygen Index (%) | 21 | | Flammability UL94 | V2 | | Volume Resistivity (log ohm.cm) | 11 | | Dielectric Strength (MV/m) | 55 | | Dissipation Factor 1kHz | 0.05 | | Dielectric Constant 1kHz | 3.6 | | HDT @ 0.45 MPa (°C) | 140 | | HDT @ 1.80 MPa (°C) | 70 | | Material. Drying hrs @ (°C) | 2 @ 90 | | Melting Temp. Range (°C) | 190 - 200 | | Mould Shrinkage (%) | 1.4 | | Mould Temp. Range (°C) | 40 - 60 | |
Applications |
| Flexible hosing for air ducts and petrol and oil pipes in the automotive and machine building industries. Nozzles, filter plates, wear plates, damping cogwheels. Cable cap closures, joints, cable fasteners. |
| Source : Abstracted from Plascams For more information on Plascams please visit RAPRA Technology Ltd. |