Stainless Steel - Grade 410 (UNS S41000)

Material: Stainless Steel - Grade 410 (UNS S41000)
Composition: Fe/<.15C/11.5-13.5Cr/<1Ni/<1Mn/<1Si/<.04P/<.03S
Property Minimum Value (S.I.) Maximum Value (S.I.) Units (S.I.) Minimum Value (Imp.) Maximum Value (Imp.) Units (Imp.)
Atomic Volume (average) 0.0071 0.0074 m3/kmol 433.268 451.575 in3/kmol
Density 7.65 7.85 Mg/m3 477.574 490.06 lb/ft3
Energy Content 84 102 MJ/kg 9100.45 11050.5 kcal/lb
Bulk Modulus 140 163 GPa 20.3053 23.6411 106 psi
Compressive Strength 275 550 MPa 39.8854 79.7708 ksi
Ductility 0.16 0.3 0.16 0.3 NULL
Elastic Limit 275 550 MPa 39.8854 79.7708 ksi
Endurance Limit 257 331 MPa 37.2747 48.0075 ksi
Fracture Toughness 36 114 MPa.m1/2 32.7617 103.745 ksi.in1/2
Hardness 1500 1900 MPa 217.557 275.572 ksi
Loss Coefficient 0.00068 0.00116 0.00068 0.00116 NULL
Modulus of Rupture 275 550 MPa 39.8854 79.7708 ksi
Poisson's Ratio 0.275 0.285 0.275 0.285 NULL
Shear Modulus 73 83 GPa 10.5878 12.0381 106 psi
Tensile Strength 485 690 MPa 70.3433 100.076 ksi
Young's Modulus 190 210 GPa 27.5572 30.4579 106 psi
Glass Temperature K °F
Latent Heat of Fusion 260 285 kJ/kg 111.779 122.527 BTU/lb
Maximum Service Temperature 973 1073 K 1291.73 1471.73 °F
Melting Point 1753 1803 K 2695.73 2785.73 °F
Minimum Service Temperature 200 230 K -99.67 -45.67 °F
Specific Heat 450 500 J/kg.K 0.348236 0.386929 BTU/lb.F
Thermal Conductivity 23 27 W/m.K 43.0568 50.5449 BTU.ft/h.ft2.F
Thermal Expansion 9 11 10-6/K 16.2 19.8 10-6/°F
Breakdown Potential MV/m V/mil
Dielectric Constant NULL
Resistivity 48 62 10-8 ohm.m 48 62 10-8 ohm.m
Environmental Properties
  Resistance Factors
1=Poor 5=Excellent
Flammability 5
Fresh Water 5
Organic Solvents 5
Oxidation at 500C 5
Sea Water 5
Strong Acid 4
Strong Alkalis 3
UV 5
Wear 4
Weak Acid 5
Weak Alkalis 5