Introduction
Super alloy Ametek 899E is a lower carbon version of commercially pure (99%) nickel. The material does contain other elements but in very small quantities adding to be than 1%.
Ametek 899E (annealed high purity nickel strip) offers the lowest electrical resistivity among pure nickel strip. It provides excellent solderability and formability.
The following sections will discuss super alloy Ametek 899E in further detail.
Chemical Composition
The chemical composition of Ametek 899E is outlined in the following table.
Element |
Content (%) |
Iron, Fe |
0.4 max |
Manganese, Mn |
0.35 max |
Silicon, Si |
0.35 max |
Copper, Cu |
0.25 max |
Carbon, C |
0.02 max |
Sulfur, S |
0.01 max |
Nickel, Ni |
Remainder |
Physical Properties
The physical properties of Ametek 899E are tabulated below.
Properties |
Metric |
Imperial |
Density |
8.88 g/cm3 |
0.321 lb/in3 |
Melting point |
1453 °C |
2647 °F |
Mechanical Properties
The following table shows mechanical properties of Ametek 899E (annealed high purity nickel strip).
Properties |
Metric |
Imperial |
Tensile strength |
421 MPa |
61100 psi |
Yield strength |
138 MPa |
20000 psi |
Poisson’s ratio |
0.31 |
0.31 |
Elongation at break |
42% |
42% |
Hardness, Vickers |
86 |
86 |
Thermal Properties
The thermal properties of Ametek 899E (annealed high purity nickel strip) are tabulated below.
Properties |
Metric |
Imperial |
Thermal conductivity(at 70°C/158°F) |
86 W/mK |
597 BTU in/hr.ft².°F |
Other Designations
Equivalent materials to Ametek 899E are tabulated below:
AMS 5553 |
ASTM B161 |
ASTM B160 |
ASTM B162 |
ASTM B366 |
ASTM B725 |
ASTM B730 |
DIN 2.4061 |
DIN 2.4068 |
ASTM B163 |
Fabrication and Heat Treatment
Machinability
Ametek 899E can be machined in the same manner as Nickel 200. It is recommended that heavy duty machining equipment and tooling be used.
Forming
Ametek 899E can be readily formed using all the traditional methods.
Forging
Forging can be done at 1148-649°C (2100-1200°F).
Welding
Welding of Ametek 899E can be performed using all the traditional welding methods except oxyacetylene welding.
Annealing
Annealing can be performed in the temperature range of 899-1300°C (1650-1300°F) depending on the temperature and the amount of cold working that has been done.
Hot Working
Hot working can be performed by heating the alloy to 1149-649°C (2100-1200°F).
Cold Working
Ametek 899E can be easily cold worked using traditional tooling.
Applications
Ametek 899E is used in the following areas:
-
Electronic components
-
Applications where spinning to form the product is required
-
Applications where chemical corrosion resistance in caustic solutions is required.